Sustained-release formulation containing an amino acid polymer with a lower alkyl (C1 -C4) polar solvent

ABSTRACT

A sustained-release polymeric hydrogel dosage form useful for topical, systemic or transdermal administration of a medicinal agent comprising a cross-linked, polymerized hydrophilic polymer, an amino acid polymer, a cross-linking agent, and an optional hydrophobic monomer and/or a chain regulator in conjunction with a lower alkyl (C 1  -C 4 ), polar solvent and said medicinal agent in a therapeutically effective amount.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates generally to a novel sustained-release formulation which gradually releases a medicinal agent therefrom. More specifically, the invention pertains to the use of the formulation for slowly dispensing a drug in the eye.

2. Description of Related Art

It is basically known in the art that medicinally active substances may be dissolved in the aqueous constituent of hydrogels to gradually release such substances over an extended period. For example, U.S. Pat. No. 3,220,960 describes utilizing a hydrogel in the eye as a carrier for time release medicaments such as boric acid or penicillin. Similarly, U.S. Pat. Nos. 3,551,556; 3,641,237; 4,003,991; and 4,271,143 disclose slowly releasing an active ingredient from an insoluble, cross-linked hydrogel in one form or another. Several compositions illustrated in the latter two patents are comprised of viscous, long-acting gel preparations where the prolongation of biological activity of the ophthalmic drug results from a slow erosion of the gel surface. The formulation in U.S. Pat. No. 3,551,556 shows granular non-ionogenic, neutral, insoluble hydrogels which are useful for oral or intramuscular application. Further, many patents are directed to ocular insert devices which prolong the effect of a drug incorporated within the device. Such patents include U.S. Pat. Nos. 3,811,444; 3,826,258; and 3,786,812.

These prior carriers of medicaments present certain difficulties during their use, particularly with ophthalmic drugs. The predominant complaint with long-acting gel formulations is blurred vision. Another difficulty is the inability to wear corrective contact lenses when a viscous material will be instilled and remain in the eye over an extended period of time. The ocular insert devices also present certain disadvantages with their use. When inserted into the conjunctival sac, such devices create a strong foreign body sensation and discomfort for the patient. The insert devices must be changed weekly. Additionally, the devices tend to fall out of the eye easily and cannot be used further by the patient since they are not capable of being sterilized.

Similarly, conventional contact lenses containing a sustained-release medicine carrier have drawbacks in practice. They have been found to obtain inadequately controlled or prolonged release characteristics making the conventional lenses unsuitable and impractical as sustained-release devices. The concept of soaking a high water content material in a drug solution has been used with conventional hydroxyethyl methacrylate based contact lenses, for example, a polymerized hydrophilic monomer or soft contact lens such as Soflens® manufactured by Bausch & Lomb. See Ruben et al., British J. Ophthal., 59:455 (1975). In practice, Soflens®, however, provides an inefficient system and is an unsuitable device for prolonged release. Experimental studies have shown that Soflens® will release 100% of pilocarpine hydrochloride in buffered saline and distilled water in merely 11/2 and 21/2 hours, respectively.

SUMMARY OF THE INVENTION

It is therefore an important object of the present invention to provide a highly unique sustained-release polymeric hydrogel dosage form which does not undergo decomposition or deterioration in body fluids and is nontoxic therein.

Another object is to provide a sustained-release polymeric hydrogel dosage form that is useful for topical, systemic or transdermal administration of medicinal agents, particularly ophthalmic drugs.

A further object is to provide a polymeric matrix which is moldable to any desired shape, with moldability to the shape of the cornea of the eye being of major interest.

A still further object is to provide a sustained-release dosage form for ophthalmic administration which does not affect eyesight and is well-tolerated and pleasing to the patient.

Another further object is to provide an opthalmic dosage form that can concurrently correct vision and release medication to the eye, i.e., a contact lens with both cosmetic and therapeutic value.

Further purposes and objects of the present invention will appear as the specification proceeds.

With the foregoing and other objects in view, the invention herein provides a sustained-release polymeric hydrogel dosage form useful for topical, systemic or transdermal administration of a medicinal agent comprising cross-linked, polymerized hydrophilic polymers, an amino acid polymer, a cross-linking agent, and optionally one or more hydrophobic polymers and/or a chain regulator in conjunction with a lower alkyl (C₁ -C₄) polar solvent and said medicinal agent in a therapeutically effective amount.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

In accordance with the present invention, the formulation employed as a sustained-release dosage form includes one or more hydrophilic polymers having an olefinic bond, an alpha-, beta-unsaturated carbonyl modified or unmodified amino acid polymer, a cross-linking agent, a lower alkyl (C₁ -C₄) alcohol and optionally one or more hydrophobic polymers and/or a chain regulator. The formulation contains a medicinal agent for the controlled-release administration to mammals of the desired active ingredient from the polymeric matrices.

The hydrophilic monomer used in the polymer of this invention can be present in varying amounts, desirably about 50% to about 90% w/w and, more preferably, about 74% to about 84% w/w of the total monomers present in the polymerization mixture. These monomers have an olefinic bond. They include, for example, the hydroxyalkyl esters and amides, both N-substituted and unsubstituted, of alpha-, beta-unsaturated carboxylic acids, N-vinyl lactams and 2-acrylamido-2-methylpropane sulfonic acid. The alpha-, beta-unsaturated acids useful in this invention are acrylic acid, crotonic acid, methacrylic acid, itaconic acid, maleic acid, maleic anhydride, fumaric acid and the like. The poly-functional alcohols which form the hydroxyalkyl esters include glycol, glycerol, propylene glycol, trimethylene glycol and other polyhydric alkanols, dialkylene glycols of 2 to 12 carbon atoms, polyalkylene glycols, etc. Polyalkylene glycols are exemplified by triethylene glycol, tetraethylene glycol, pentaethylene glycol, hexaethylene glycol and the like. The preferred hydrophilic monomers are the hydroxyalkyl esters, specifically hydroxyethyl methacrylate (HEMA).

Useful amides of the foregoing acids include diacetone acrylamide and N-mono-substituted diacetone acrylamide. Also useful are the amines of the foregoing acids such as mono- or di-alkylamino substituents.

A nitrogen containing monomer which may be used in the preparation of the polymers and copolymers of this invention is conveniently referred to as N-vinyl lactam which includes (a) N-vinyl lactams per se and (b) other heterocyclic N-vinyl monomers. Illustrative of the N-vinyl lactams that are employed in this invention are N-vinyl-2-pyrrolidinone, N-(1-methyl vinyl) pyrrolidinone, N-vinyl-2-piperidone, N-vinyl-2-caprolactam and the like which may be substituted in the lactam ring by one or more lower alkyl groups such as methyl, ethyl or propyl, e.g., N-vinyl-5-methyl pyrrolidnone, N-vinyl-3,3-dimethyl pyrrolidinone, N-vinyl-5-ethyl pyrrolidinone, N-vinyl-6-methyl piperidone, etc. Illustrative of the other heterocyclic N-vinyl monomers used in preparing the polymers of this invention are N-vinyl imidazole, N-vinyl succinimide, N-vinyl diglycolylimide, N-vinyl glutarimide, N-vinyl-3-morpholinone, N-vinyl-5-methyl-3-morpholinone, etc. The lactams may be effectively employed alone or in admixture with other lactam monomers to give hydrogels having the foregoing desirable characteristics.

The second monomeric component forming the polymer of this invention is an alpha-, beta-unsaturated carbonyl modified or unmodified amino acid monomer or monomers. This component can be present in varying amounts, desirably in an amount from about 5% to about 27% w/w and, more preferably, about 6% w/w of the total monomers present in the polymerization mixture. The modified or unmodified amino acid monomers are hydrophilic compounds which contribute significantly to the swelling of the polymer in water and permit higher oxygen diffusion.

The alpha-, beta-unsaturated carbonyl modifier for the modified amino acids of this invention may be, for example, acrylic acid, crotonic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid and their functional derivatives, i.e., acid chlorides, anhydrides, amides and esters. The more preferred modifiers are methacrylic acid and methacroyl chloride.

An amino acid is an organic acid whose molecule contains both a carboxyl group (COOH) and an amino group (NH₂) coupled with an alkyl, cycloalkyl, aryl or heterocyclic structure, the alkyl, cycloalkyl or heterocyclic structure being free of olefinic unsaturation. The alpha-, beta-carbonyl substituent can be attached to either the amino group or the hydroxy group of the amino acid, depending on the structure of the amino acid. Additionally, the carbonyl substituent can attach to other reactive groups, if present, in the amino acid, e.g., thiol (SH) or phenolic hydroxyl.

Amino acids useful in the preparation of the modified acids of this invention include, but are not limited to, beta-alanine, gamma-aminobutyric acid, omega-aminocaproic acid, omega-aminododecanoic acid, beta-cycanoalanine, epsilon-methylhistidine, canavanine, djenkolic acid, 1-azaserine, gammamethylene glutamic acid, N-methyltyrosine, glycine, alanine, serine, cystine, cysteine, lanthionine, phenylalanine, tyrosine, diiodotyrosine, tryptophan, histidine, aminobutyric acid, methionine, valine, norvaline, leucine, isoleucine, norleucine, arginine, ornithine, lysine, aspartic acid, glutamic acid, threonine, hydroxyglutamic acid, proline, hydroxyproline, asparagine, glutamine, desmosine, isodesmosine, 5-hydroxylysine and the like. Preferred amino acids are glycine, glutamic acid, desmosine and isodesmosine.

It should be understood that other, though perhaps less common, amino acids occurring in nature or prepared synthetically, including those shown in the examples which follow, are within the scope of this invention. Reactive sites on the amino acids can be partially blocked by saturated nonpolymerizable substituents provided that one reactive site is substituted by the alpha-, beta-carbonyl substituent.

The polymers used in this invention are cross-linked by all types of cross-linking compounds used in the prior art, see for instance, U.S. Pat. Nos. 3,822,089; 4,152,508; and 4,440,919. The cross-linking agent can be employed in varying amounts and desirably in an amount from about 3 to about 30 parts by weight of the total monomers present. Examples of cross-linking agents include polyfunctional derivatives of the previously enumerated alpha-, beta-unsaturated acids, e.g., acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid, fumaric acid, acrylamide, methacrylamide, multivinyl substituted benzenes, etc. More particularly these cross-linking agents include, but are not limited to, the following: ethylene glycol diacrylate or dimethacrylate, diethylene glycol diacrylate or dimethacrylate, triethylene glycol diacrylate or dimethacrylate, tetraethylene glycol diacrylate or dimethacrylate, polyethylene glycol diacrylate or dimethacrylate, trimethylolpropane triacrylate or trimethacrylate, bisphenol A diacrylate or dimethacrylate, ethoxylated bisphenol A diacrylate or dimethacrylate, pentaerythritol tri- and tetra-acrylate or methacrylate, tetramethylene diacrylate or dimethacrylate, methylene bisacrylamide or methacrylamide, dimethylene bisacrylamide or methacrylamide, N,N'-dihydroxyethylene bisacrylamide or methacrylamide, hexamethylene bisacrylamide or methacrylamide, decamethylene bisacrylamide or methacrylamide, divinyl benzene, vinyl methacrylate, allyl methacrylate, etc. A preferred cross-linking agent is allyl methacrylate.

Still other useful cross-linking agents include 1,3-bis (4-methacryloyl oxyalkyl) tetra disiloxane and similar poly (organo-siloxane) monomers set forth in U.S. Pat. No. 4,153,641. Another group of useful cross-linking agents are the resonance free di(alkylene tertiary amine) cyclic compounds, e.g., N,N'-divinyl ethylene urea, as disclosed in U.S. Pat. No. 4,436,887. Yet another group are di- or polyvinyl ethers of di- or polyvalent alchols such as ethylene glycol divinyl ether.

The formation of the instant invention also contains a lower alkyl (C₁ -C₄) polar solvent, preferably volatile, demonstrating high water solubility parameters such as a lower alkyl (C₁ -C₄) alcohol, an unmodified or modified ketone and the like for controlling the viscosity of the polymer. Suitable solvents may also include mixtures of modified and unmodified ketones in any proportions and mixtures of a lower alkyl (C₁ -C₄) alcohol and water in any proportions. Examples of solvents are methanol, ethanol, propanol, butanol, isopropanol, acetone, methyl ethyl ketone, hydroxyacetone, etc. Typically, equal parts of solvent and linear, polymerized polymer are used in the preparation of the formulation. However, different amounts of the solvent may be used with the polymer though generally less conveniently. When the process of this invention is followed, the residue of the solvent remains in the formulation in varying amounts depending upon reaction conditions such as time and temperature. Preferably trace amounts of the residue are present for ophthalmic use and higher amounts are present for transdermal use.

Optionally, a chain regulator or chain transfer agent may be added if a particular monomer-solvent combination requires it. For example, certain combinations containing solvents such as butanol may require large quantities of butanol which may not be desirable in the product. If a chain regulator is added, a smaller amount of butanol may be used.

The term "chain regulator" refers to any chemical that controls the molecular weight of the polymer during polymerization. A chain regulator may be optionally employed in varying amounts and desirably in an amount from about 0.01% w/w to about 0.5% w/w. Examples of chain regulators include, but are not limited to, dodecanethiol, isopropyl mercaptan, decanethiol and the like. A particularly preferred chain regulator is dodecanethiol.

For some applications the polymerizates formed from the above hydrophilic monomer(s), modified or unmodified amino acid monomer(s), cross-linking agent(s), a lower alkyl (C₁ -C₄) alcohol and an optional chain regulator may lack the desired physical handling properties. It is another aspect of this invention in such circumstances to incorporate one or more hydrophobic monomers in the above polymers in varying amounts, desirably from about 8% to about 20% w/w of the total monomers present. More preferably the hydrophobic monomer would be present in an amount of about 10% w/w of the total monomers present. Among other things, the hydrophobic monomers are useful as modulus modifiers.

The modulus modifier may be, for example, cycloalkyl ester, tertiarybutyl styrene, polycyclic acrylate or methacrylate, and the like as well as mixtures thereof. More particularly the polycyclic modifiers may be isobornyl acrylate, isobornyl methacrylate, dicyclopentanedienyl acrylate, dicyclopentanedienyl methacrylate, adamantyl acrylate, adamantyl methacrylate, isopinocamphyl acrylate, isopinocamphyl methacrylate, etc. and mixtures thereof. The cycloalkyl ester modifier is of formula I below. Illustrative of these cycloalkyl modifiers are menthyl methacrylate, menthyl acrylate, tertiarybutyl cyclohexyl methacrylate, isohexyl cyclopentyl acrylate, methylisopentyl cyclooctyl acrylate and the like. ##STR1## wherein: D is branched or normal alkyl of 3 to 6 carbon atoms

E is H or CH₃

Z is H or CH₃

n is an integer from 3 to 8.

In addition to the modulus modifiers other well known hydrophobic monomers may be used in the formulation of the polymers and copolymers of this invention to further tailor the properties to the particular application. The hydrophobic monomers of this invention include monomers which contain at least one silicon or fluorine atom as a part of its composition. Hydrophobic monomers include alkyl, cyclo-alkyl and aryl acrylates and methacrylates as well as mono- or disubstituted itaconates, styrene and its derivatives, acrylonitrile, vinyl esters such as vinyl acetate or vinyl pentacetyl gluconate, vinyl ethers such as vinyl butyl ether, allyl esters such as allyl acetate, propionate or butyrate, fluorine containing monomers such as octafluoropentyl methacrylate and silicon containing monomers, e.g., 1,1,1-tris (trimethoxysiloxy)-3-methacryloxy-propylsilane or heptamethyltrisiloxanyl ethyl acrylate.

The monomeric mixtures, comprising the hydrophilic monomer(s), the modified or unmodified amino acid monomer(s), the optional hydrophobic monomer(s), the cross-linking agent, the lower alkyl (C₁ -C₄) alcohol and the optional chain regulator are generally clear, colorless liquids of varying viscosity. These monomer mixtures are polymerized but not cross-linked using ultraviolet light at room temperature. According to the process of this invention, the medicinal agent dissolves in this linear, polymerized polymer that can then be cross-linked by ultraviolet light and/or heat. Before crosslinking takes place, the linear polymer is characterized by being soluble in methanol and isopropanol. After cross-linking, an insoluble polymer is formed.

As catalysts for carrying out the polymerization, there may be employed a free radical catalyst (initiator) in varying amounts and typically in the range of about 0.05% to 3% w/w of the polymerizable monomer mixture. The preferred amount of catalyst is 0.1% to 2.5% w/w of the total monomers present. Usually, the catalyst is added initially to the monomers and then the polymerization procedure is completed. The free radical type initiators suitable for this invention include peroxides, azo compounds, oxidation-reduction systems and similar initiators described in the literature. Typical catalysts include benzoin methyl ether, tertiary-butyl-peroctoate, benzoyl peroxide, isopropyl percarbonate, methyl ethyl ketone peroxide, cumene hydroperoxide, dicumyl peroxide, bis(isopropyl) peroxydicarbonate, 2,2'-azobis[isobutyronitrile], acetyl peroxide, lauroyl peroxide, decanoyl peroxide, 2,2'-azobis[2,4-dimethylvaleronitrile], phthalic peroxide, diethoxyacetophenone, tertiary-butyl peroxypivalate and the like. Thermal catalysts, visible light or irradiation, e.g., by ultraviolet light or gamma rays, also can be employed to catalyze the polymerization. Polymerization can be done at 20° to 150° C., usually 40° to 90° C. Prior to adding a medicament or to cross-linking the polymer, a prepolymerization of the monomer mix may be achieved at room temperature, usually 20° to 28° C., to create a linear, polymerized polymer. Cross-linking may be done using a suitable amount of heat, typically 65° to 75° C. The choice of catalyst obviously depends upon the temperature desired for the reaction.

Water soluble diluents may be used with the foregoing polymers to modify the physical properties of these polymers. More particularly, the diluents may be advantageous in improving machinability and swell characteristics of the polymer. Typically, the amount of diluent will be less than 50 weight percent of the total monomers employed and preferably not more than 30 weight percent. In a particular polymer system, the limiting amount of diluent is the solubility of the diluent in the monomer system. Thus, there should be no phase separation between diluent and starting monomer mixture. Additionally, excessive amounts of diluent will result in collapse of the cell structure of the finished biomedical devices when the device is hydrated, i.e., replacement of diluent by water. The maximum amount of diluent is readily ascertained by swelling the diluent free polymer in the proposed diluent and measuring the degree of swell. Comparable results are obtained when using solvent soluble diluents wherein the solvent does not affect the lens polymer. Suitable diluents include ethylene glycol, glycerin, liquid polyethylene glycols, butanol, butanol/water mixtures, ethylene oxide/propylene oxide block copolymers having a molecular weight from 1,000 to 5,000, linear poly(vinyl pyrrolidinone) having a molecular weight from 500 to 10,000, low molecular weight linear poly(hydroxyethyl methacrylate), glycol esters of lactic acid, formamide, dimethyl formamide, dimethyl sulfoxide and the like. In the finished biomedical device, it will be necessary to replace any diluent with an aqueous solution. With respect to contact lenses, the final water content of the polymeric composition typically ranges from about 25% to about 70% w/w. The contact lens should, of course, contain a physiological saline solution as the aqueous medium.

Using methods well known in the art, the sustained-release formulation of this invention can be formed into a variety of shapes depending upon the end use and desired results to be obtained therefrom. For ophthalmic purposes, the polymeric hydrogel could have any form to maintain direct contact with the eye. It is not necessary to cover the entire cornea if the dosage form is merely used to instill a continuous flow of an ophthalmic drug in the eye. If the hydrogel will also be used to correct vision, then it may be desirable to cast the polymer on an optical mold.

By way of example, the mixture of hydrophilic monomer(s), modified or unmodified amino acid monomer(s), cross-linking agent, free radical initiator and optional hydrophobic monomer(s) described above is prepared. If desirable, a chain regulator is added to this mixture. Then a lower alkyl (C₁ -C₄) alcohol is added. A two-stage process is carried out by forming a linear, polymerized polymer by ultraviolet light at room temperature and crosslinking the polymer by subsequent application of heat together with ultraviolet light if needed.

This invention contemplates a process for preparing the sustained-release polymeric hydrogel dosage form whereby the medicinal agent is retained by the polymeric matrix and, upon tissue contact, is gradually released into the tissue. The medicinal agent may be dissolved directly into the linear, uncross-linked polymer. The drug becomes intimately mixed in the polymeric matrix rather than remaining as particulate matter. Subsequent cross-linking prevents co-polymerization of the drug with the polymer allowing for greater recovery of the drug upon tissue contact. The drug would release slowly into the tissue for local or systemic effect over prolonged time intervals at lower concentrations thereby eliminating or reducing side effects. The amount of the drug used in the preparation of the dosage forms will vary depending upon the physicochemical properties of the selected drug and the therapeutic effect desired to be achieved. Typically, the drug is added on a equivalency basis, that is, an equivalent for equivalent basis of drug to the linear, polymerized polymer. Although a stoichiometric number of equivalents of drug and the linear, polymerized polymer is preferred, other amounts can also be used. As an example of pilocarpine hydrochloride, varying concentrations of the compound may be employed, desirably an amount from about 5% to about 15% w/w, of pilocarpine hydrochloride to the weight of the linear polymer, and preferably 9.1% w/w, for incorporation in the dosage form.

The polymeric composition of the instant invention provides appreciable time release of the medicament. The release rate of a drug from the polymeric matrix varies with cross-linking density and type of polymer barrier system. Additionally, the release rate depends upon the viscosity of the linear, uncross-linked polymer which is controlled by the addition of a polar, volatile solvent such as a lower alkyl (C₁ -C₄) alcohol.

To quantify the release rates, lenses with and without drug can be placed in a known quantity of release media (distilled water or buffered saline) and stirred with a magnetic stirrer. At various times the lenses can be transferred to fresh media and the absorbance of the previous media can be determined by ultraviolet spectroscopy. The absorbance of the media containing drugged lenses is reduced by the absorbance of the media containing undrugged lenses. Use of a calibration curve relating absorbance to concentration allows for a determination of the concentration of the drug. The calibration curve is developed by measuring the absorbance of known concentrations of the drug in the release media. As the concentrations (μg/ml) of the drug and the volume (ml) of release media are known, the amount of the released drug can be calculated (μg). This value divided by the time of exposure to the media gives the release rate in μg/hr which is plotted against time.

The contact lenses made from the polymer utilized in the instant invention are oxygen permeable. A critical oxygen tension and flux under a lens should be about 10 mm Hg and 2 μl/(cm² hr.) respectively below which corneal swelling occurs, see Polse and Decker, Investigative Ophthalmology and Visual Science, 18:188 (1979). In order to meet these requirements, the lens material must have adequate oxygen permeability. These more preferred contact lenses have an oxygen permeability of at least about 24×10-¹¹ cm³ cm/(sec.cm² mmHg), are hydrolytically stable, biologically inert and transparent. In comparison, the well-known contact lens polymer polyhydroxyethyl methacrylate has an oxygen permeability value of about one-third of the polymers of this invention.

Additionally, these lenses are hydrolytically stable, meaning that when the contact lenses are placed into an aqueous solution (e.g., on the eye) or during the disinfecting step (i.e., water plus heat), the lenses will not change in chemical composition. That is, they will not hydrolyze. On heating in boiling water for 120 hours, the typical polymer of this invention experiences a water content loss of 3% or less. The most preferred lenses/polymers useful in this invention have a stable water content that undergoes less than 1% change. Thus, the polymers and copolymers disclosed herein can be boiled and/or autoclaved in water without being damaged whereby sterilization may be achieved. In addition, sterilization can be achieved by gamma-irradiation, ultraviolet light irradiation and ethylene oxide exposure.

The polymers and copolymers employed in this invention being soft yet resilient and hard to tear are well suited for preparing biomedical devices, including contact lenses, which have the ability to release medications from the polymeric matrix over a prolonged period of time. It is well known that the wearer of soft contact lenses will have an unavoidable amount of handling of the lenses. Part of the cleaning and rinsing procedure is to rub each lens and tearing has been a concern in prior art lenses. The polymers and copolymers used in the present invention have a tear initiation strength (ASTM D-1938) of up to 5 g/mm of thickness.

An article formed from the disclosed polymers and copolymers may be used to administer medications to mammals where an article compatible with living tissue or with the mucous membranes is desired. The term "biomedical devices" means the materials disclosed herein have nontoxic, nonirritating physiochemical properties rendering them suitable for prolonged contact with living tissue, blood and the mucous membranes. It is known that blood, for example, is rapidly damaged in contact with artificial surfaces. The design of a synthetic surface which is antithrombogenic and nonhemolytic to blood is necessary for drug administering devices used with blood, especially an implanted or transdermal device. The polymers and copolymers employed for the purposes of the instant invention are compatible with living tissue.

The instant invention provides a novel sustained-release polymeric hydrogel dosage form useful for topical, systemic or transdermal administration of a medicinal agent comprising the above-described polymeric matrix in association with a therapeutically effective amount of the medicinal agent. When prepared according to the novel process of this invention, the polymeric matrix permits the active ingredient to be subsequently released at a gradual, carefully controlled rate prolonging the time release period. Further, this invention concerns a method of administering a therapeutically effective amount of a medicinal agent over an extended period of time to a mammal in need of the medicinal agent which comprises contacting a tissue of said mammal with the sustained-release polymeric hydrogel dosage form for a sufficient amount of time to achieve a constant therapeutic effect. In contrast to normal disintegration time, the sustained-release administration of medicaments enhances therapeutic effectiveness and decreases many undesirable side effects by maintaining constant tissue and blood levels.

The polymeric hydrogel dosage form can be used in preparing biomedical devices that upon surgical implant will provide sustained-release activity of the active ingredient. Depending on the location of the implant, the therapeutic effect may be local or systemic. The dosage form can also provide for the oral or topical (i.e., localized activity on the skin) controlled-release administration of medicaments. Additionally, the dosage form can be utilized for the transdermal controlled-release administration of medicaments, i.e., the device is retained in contact with the skin for transdermal absorption of the medicament into the blood for systemic effect. Contact with the skin may be achieved by any means well-known in the art such as by incorporating an adhesive in or on the device, adhering the device within or onto a bandage-type article, etc.

Further, the dosage form can be useful for the ophthalmic route of administering medicinal agents for either local or systemic therapeutic effect. The term "ophthalmic administration of a systemic medicament" defines the administration of a medicinal agent to a mammal by the ophthalmic route whereby the medicinal agent acts therapeutically to create a systemic effect. For ophthalmic administration of a medicament to produce local or systemic activity, the polymeric composition can be molded into any convenient shape for eye contact. If correcting vision is not necessary, the dosage form does not have to cover the entire cornea. Alternatively, the polymeric hydrogel can be shaped into contact lenses on optical molds if it is desirable to correct vision in addition to administer ophthalmic medicaments.

The length of time for contacting the polymeric hydrogel device containing a medicament with a tissue of a mammal depends upon the individual circumstances of each case. A sufficient amount of time to achieve a constant therapeutic effect varies in accordance with the optimum therapeutic effect desired. The duration of therapy is, of course, contingent upon the disease or medical problem being treated or palliated. Likewise, the therapeutically effective amount of the specific medicinal agent is determined by therapy requirements and the biophysical properties of the active compound. For example, with respect to contact lenses, the invention contemplates daily wear or extended wear, typically, up to a month. To treat an eye infection, it would be desirable to maintain the contact lens containing an antibiotic or an antiviral agent on the eye for one to two weeks. On the other hand, to treat glaucoma, it would be desirable to wear the lens containing an agent for reducing intraocular pressure for the maximum time that extended wear contact lenses can remain in the eye.

The term "dosage form" refers to physically discrete units suitable as unitary dosage for mammals, each unit containing a predetermined quantity of active component calculated to produce the desired therapeutic effect. The novel sustained-release dosage form of this invention is indicated by the physical or chemical characteristics of the active component and the particular therapeutic effect to be achieved.

The term "a medicinal agent" means a substance used in treating or ameliorating a disease or medical condition. For purposes of this invention, "a medicinal agent" refers to drugs which would have the capacity to be bound to the amino acid moiety of the polymeric hydrogel. That is, any drug or its salt with polar characteristics that interacts with amino acids in a favorable way could be used in the present invention. Examples of medicinal agents include, but are not limited to, antibiotics, antivirals, anti-inflammatories, steroids, peptides, polypeptides, cardiotonics, antihypertensives, antiallergics, alpha- and beta-adrenergic blocking agents, anticataract agents, ophthalmic medicaments, ophthalmic lubricating agents, ophthalmic topical or regional anesthetic agents, etc. The ophthalmic medicaments or other medicinal agents encompass such drugs as pilocarpine, idoxuridine, carbachol, bethanechol, timolol, tetracycline, epinephrine, phenylephrine, eserine, phospholine, demecarium, cyclopentolate, homatropine, scopolamine, nitroglycerin, chlortetracycline, bacitracin, neomycin, polymyxin, gramicidin, oxytetracycline, chloramphenicol, gentamycin, penicillin, erythromycin, sulfacetamide, polymyxin B, tobramycin, isofluorophate, fluoromethalone, dexamethasone, hydrocortisone, fluorocinolone, medrysone, prednisolone, methyl prednisolone, betamethasone, triamcinolone, interferon, cromolyn, all-trans-retinoic acid (Vitamin A), the nontoxic, pharmaceutically acceptable salts thereof and the like. The category of ophthalmic lubricating agents refers to those agents capable of inducing natural lacrimation or creating artificial lacrimation and includes, for example, polyvinyl alcohol, cellulose polymers such as hydroxypropyl methyl cellulose, a polylactam such as polyvinylpyrrolidinone and other tear inducers or substitutes. The topical or regional anesthetic agents, which may be useful during ophthalmic surgery or other ophthalmic procedures, include lidocaine, cocaine, benoxinate, dibucaine, proparacaine, tetracaine, etidocaine, procaine, hexylcaine, bupivacaine, mepivacaine, prilocaine, chloroprocaine, etc.

The term "pharmaceutically acceptable salt" refers to those salts of the parent compound which do not significantly or adversely affect the pharmaceutical properties (e.g., toxicity, efficacy, etc.) of the parent compound. The salts of the present invention which are pharmaceutically acceptable include, for example, chloride, iodide, bromide, hydrochloride, acetate, nitrate, stearate, phosphate, sulfate, etc. It is desirable to use the appropriate salt form of the active ingredient which would increase the water solubility or polar characteristics of the base compound.

In addition to the medical uses, the above described polymeric hydrogel may be found useful with veterinary products and agricultural chemicals such as pesticides, herbicides and the like. For example, a pesticide incorporated into the polymer may be mixed with fertilizers. On spraying, the alcohol evaporates leaving a film which could be made biodegradable.

The following examples demonstrate certain aspects of the present invention. However, it is to be understood that these examples are for illustrative purposes only and do not purport to be wholly definitive as to conditions and scope of this invention. All parts and percents referred to herein are on a weight basis and all temperatures are expressed in degrees Celsius unless otherwise specified. It also should be appreciated that when typical reaction conditions (e.g., temperature, reaction times) have been given, the conditions which are both above and below these specified ranges can also be used, though generally less conveniently.

A further understanding of the invention may be obtained from the following nonlimiting examples. These examples were conducted at room temperature (about 23° C. to about 28° C.) and at atmospheric pressure.

EXAMPLE 1 Preparation of a Hydrogel Polymer Containing Pilocarpine Hydrochloride

A mixture is prepared by combining 74.5 g of 2-hydroxyethyl methacrylate (HEMA) containing 0.12% of ethylene glycol dimethacrylate (EGDMA), 10 g of isobornyl methacrylate (IBOMA), 6 g of methacroyl glycine (MG), 2.5 g of benzoin methyl ether (BME) and 0.1 g of 2, 2'-azobis[isobutyronitrile]. To the mixture is added 5 g of allyl methacrylate. To 5 g of the mixture is added 5 g of methanol. This mixture is then purged with nitrogen and polymerization is performed with stirring under ultraviolet light (UV) at room temperature for 2 hours. When a honey-like consistency develops, 0.205 g of pilocarpine hydrochloride is added to 4 g of the linear polymer forming a clear solution. The solution is cross-linked with a subsequent exposure to UV for 30 minutes at room temperature and then to UV for 30 minutes at 70° C.

EXAMPLE 2 Preparation of a Hydrogel Polymer Containing Pilocarpine Hydrochloride

The procedure of Example 1 is repeated to prepare the hydrogel polymer with the additional step of adding 0.01 g of dodecanethiol after the allyl methacrylate is added to the mixture.

EXAMPLE 3 Preparation of a Hydrogel Polymer Containing Pilocarpine Hydrochloride

The procedure of Example 1 is repeated to prepare the hydrogel polymer with the additional step of adding 0.02 g of dodecanethiol after the allyl methacrylate is added to the mixture.

EXAMPLE 4 Preparation of a Hydrogel Polymer Containing Pilocarpine Hydrochloride

The procedure of Example 1 is repeated to prepare the hydrogel polymer with the additional step of adding 0.25 g of dodecanethiol after the allyl methacrylate is added to the mixture.

EXAMPLE 5 Preparation of a Hydrogel Polymer Containing Pilocarpine Hydrochloride

The procedure of Example 1 is repeated to prepare the hydrogel polymer with the additional step of adding 0.5 g of dodecanethiol after the allyl methacrylate is added to the mixture.

EXAMPLE 6 Preparation of a Hydrogel Polymer Containing Nitroglycerin

The hydrogel polymer of this example is prepared according to the procedure of Example 1 except that 0.025 g of nitroglycerin is substituted for the pilocarpine hydrochloride.

EXAMPLE 7 Preparation of a Hydrogel Polymer Containing Scopolamine

The hydrogel polymer of this example is prepared according to the procedure of Example 1 except that 0.2 g of scopolamine is substituted for the pilocarpine hydrochloride.

In the foregoing there has been provided a detailed description of preferred embodiments of the present invention for the purpose of illustration and not limitation. It is to be understood that all other modifications, ramifications and equivalents obvious to those having skill in the art based on this disclosure are intended to be within the scope of the invention as claimed. 

What is claimed is:
 1. A sustained-release polymeric hydrogel dosage form useful for topical, systemic or transdermal administration of a medicinal agent comprising a cross-linked, polymerized hydrophilic polymer including an amino acid moiety in the polymer, in conjunction with a lower alkyl (C₁ -C₄) polar solvent and said medicinal agent in a therapeutically effective amount.
 2. The sustained-release dosage form of claim 1 wherein the polymer includes therein a hydrophobic component:
 3. The sustained-release dosage form of claim 1 or 2 wherein the amino acid moiety is derived from an aliphatic monocarboxylic acid, an aliphatic dicarboxylic acid, an aromatic dicarboxylic acid, an aromatic tricarboxylic acid or an aromatic tetracarboxylic acid.
 4. The sustained-release dosage form of claim 1 or 2 wherein the amino acid moiety is derived from methacroyl glycine, methacroyl glutamate, methacroyl desmosine or methacroyl isodesmosine.
 5. The sustained-release dosage form of claim 1 or 2 wherein the polar solvent is a lower alkyl (C₁ -C₄) alcohol, an unmodified ketone, a modified ketone, a mixture of a lower alkyl (C₁ -C₄) alcohol and water in any proportion or a mixture of an unmodified ketone and a modified ketone in any proportion.
 6. The sustained-release dosage form of claim 1 or 2 wherein said medicinal agent is an antibiotic, an antiviral, an anti-inflammatory, a steroid, a peptide, a polypeptide, a cardiotonic, an antihypertensive, an antiallergic, an alpha-adrenergic blocking agent, a beta-adrenergic blocking agent, an anticataract agent, an ophthalmic medicament, an ophthalmic lubricating agent or an ophthalmic anesthetic agent.
 7. The sustained-release dosage form of claim 1 or 2 wherein said medicinal agent is selected from the group consisting of pilocarpine, idoxuridine, carbachol, bethanechol, timolol, tetracycline, epinephrine, phenylephrine, eserine, phospholine, demecarium, cyclopentolate, homatropine, scopolamine, nitroglycerin, chlortetracycline, bacitracin, neomycin, polymyxin, gramicidin, oxytetracycline, chloramphenicol, gentamycin, penicillin, erythromycin, sulfacetamide, polymyxin B, tobramycin, isofluorophate, fluoromethalone, dexamethasone, hydrocortisone, fluorocinolone, medrysone, prednisolone, methyl prednisolone, betamethasone, triamcinolone, interferon, cromolyn, all-trans-retinoic acid and a nontoxic, pharmaceutically acceptable salt thereof.
 8. The sustained-release dosage form of claim 1 or 2 wherein said medicinal agent is an ophthalmic lubricating agent selected from the group consisting of polyvinyl alcohol, a cellulose polymer and a polylactam.
 9. The sustained-release dosage form of claim 1 or 2 wherein said medicinal agent is an ophthalmic anesthetic agent.
 10. The sustained-release dosage form of claim 1 or 2 wherein said dosage form is molded as a contact lens or ocular insert for ophthalmic administration of a systemic medicament, an ophthalmic medicament or an ophthalmic lubricating agent.
 11. The sustained-release dosage form of claim 1 or 2 wherein said dosage form is molded as a contact lens for opthalmic administration of a systemic medicament, an ophthalmic medicament or an ophthalmic lubricating agent and retains the ability to correct vision.
 12. The sustained-release dosage form of claim 2 wherein a polymeric hydrogel is prepared from a polymerizable hydrophilic monomer present in the amount of about 50% to about 90% w/w, an amino acid monomer present in the amount of about 5% to about 27% w/w, a cross-linking agent present in the amount of about 3% to about 30% w/w and a hydrophobic monomer present in the amount of about 8% to about 20% w/w, the weight percent being based on the total weight of the polymeric hydrogel.
 13. A method of administering a therapeutically effective amount of a medicinal agent over an extended period of time to a mammal in need of the medicinal agent for local or systemic effect which comprises contacting a tissue of said mammal with the sustained-release dosage form of claim 1 or 2 for a prolonged period of time.
 14. A method of administering a therapeutically effective amount of an ophthalmic medicament over an extended period of time to a mammal in need of the medicament which comprises contacting an eye tissue of said mammal with the sustained-release dosage form of claim 1 or 2 for a prolonged period of time, wherein said medicinal agent is the opthalmic medicament.
 15. A method of administering a therapeutically effective amount of an ophthalmic lubricating agent over an extended period of time to a mammal in need of the agent which comprises contacting an eye tissue of said mammal with the sustained-release dosage form of claim 1 or 2 for a prolonged period of time, wherein said medicinal agent is the ophthalmic lubricating agent.
 16. A method of administering a therapeutically effective amount of an ophthalmic anesthetic agent over an extended period of time to a mammal in need of ophthalmic anesthesia which comprises contacting an eye tissue of said mammal with the sustained-release dosage form of claim 1 or 2 for a prolonged period of time, wherein said medicinal agent is the ophthalmic anesthetic agent.
 17. A method of treating glaucoma in a mammal suffering from glaucoma which comprises contacting an eye tissue of said mammal with the sustained-release dosage form of claim 1 or 2, wherein said medicinal agent is an agent for reducing intraocular pressure for a prolonged period of time.
 18. A method of treating glaucoma in a mammal suffering from glaucoma which comprises contacting an eye tissue of said mammal with the sustained-release dosage form of claim 1 or 2, wherein said medicinal agent is timolol, pilocarpine or a nontoxic, pharmaceutically acceptable salt thereof for a prolonged period of time.
 19. A method of inducing natural lacrimation or creating artificial lacrimation in a mammal suffering from deficient lacrimation which comprises contacting an eye tissue of said mammal with the sustained-release dosage form of claim 1 or 2 for a prolonged period of time, wherein said medicinal agent is an ophthalmic lubricating agent.
 20. A process for the preparation of the sustained-release dosage form of claim 1 which comprises mixing a hydrophilic monomer, an amino acid monomer, a cross-linking agent and a lower alkyl (C₁ -C₄), polar solvent, polymerizing at room temperature, adding a medicinal agent and cross-linking.
 21. A process for the preparation of the sustained-release dosage form of claim 2 which comprises mixing a hydrophilic monomer, an amino acid monomer, a cross-linking agent, a hydrophobic monomer and a lower alkyl (C₁ -C₄), polar solvent, polymerizing at room temperature, adding a medicinal agent and cross-linking.
 22. The process of claim 20 or 21 wherein a catalyst is used.
 23. The process of claim 20 or 21 wherein a chain regulator is added.
 24. The process of claim 20 or 21 wherein a catalyst is used and a chain regulator is added. 